Adhesive sealant KMD398 for 10g ultrasonic elements

Adhesive sealant for fixing ultrasonic elements
Adhesive sealant KMD398 for 10g ultrasonic elements
NOT available.
Expected price: 75,60 UAH
from 1 pc : 75,60 UAH
from 5 pcs : 71,82 UAH ( -5,0%)
Prices are indicated at the time of product availability and may change upon receipt

Current balances:

NOT available

Изображение товара

Product description format_size zoom_out zoom_in

A specialized two-component adhesive-sealant for ultrasonic elements based on modified acrylate. Has excellent adhesion, increased relaxation ability (anti-fatigue), high shock and vibration resistance, excellent tensile strength, no cold shrinkage (low coefficient of thermal expansion), resistance to elevated temperatures (≥200°C), water resistance and resistance to various chemical corrosion ... It has good stability and consistency, and is suitable for bonding emitters to tanks of ultrasonic cleaning machines and industries with high demands on various working conditions. It can be used for bonding various metal alloys, stainless steel, aluminum and ceramics.
 
The adhesive sealant is based on a new generation of modified acrylate and has a simple ratio of 1: 1 components (by volume), which simplifies the production process of ultrasonic devices.
 
Under cyclic loads of adhesive joints, relaxation processes take place in them. As the temperature rises or during the plasticization of the adhesive, the relaxation rate increases, as a result of which the strength decreases more slowly, but at the same time the fatigue limit also decreases. In other words, in joints based on adhesives with an increased relaxation ability, the process of damage accumulation associated with crack growth is slowed down.
 
 

Main characteristics:

  • Material: modified acrylate+hardener
  • Mixing ratio (by volume): 1: 1
  • Viscosity: 5-8 Pa * s
  • Plasticization time:
  • - initial setting: after 10 minutes
  • - basic durability: after 2 hours
  • - maximum durability: after 10 hours
  • Temperature resistance: -60°C ~ ≥ +200°C
  • Shear strength: ≥ 33.8 MPa (24 hours at room temperature)
  • Tensile strength: ≥32.2 MPa (24 hours at room temperature)

Table of dependence of strength characteristics on temperature:

Temperature (°C)    20 °C   100 °C   120 °C   150 °C     180 °C    200 °C
Shear strength (MPa)    33.8    28.8   20.5   18.6      6.7    5.4
Tensile Strength (MPa)    32.2    23.6   19.7   18.2      6.9    4.7

* Test conditions: test pieces after curing for 24 hours and after a set temperature for 15 minutes.

Leave your feedback or ask a question

Only this product is discussed here. Off topic comments will be deleted! Please follow the Commenting Rules.

The data presented in the product description are for reference only and may differ from those indicated by the manufacturer.
To carry out technical calculations and obtain the exact parameters of the goods, use the datasheets from the manufacturer's website.

If you need additional information, or you found an error in the description, or have other questions about this product, then our manager will help you: Денис - Днепр unknown

Buy with this product: Посмотреть больше…