Universal white adhesive sealant Ausbond 704 (RTV Silicone Rubber), tube 100 ml
The main properties of Ausbond 704 RTV are high adhesion strength, very high insulating properties. High temperature range.
Provides a strong connection.
Resistant to mold, mildew, ultraviolet light, moisture and environmental factors.
Moderately resistant to aromatic solvents and concentrated acids.
High resistance to household chemicals.
Easy to process after curing, can be overpainted.
Non-corrosive.
Scope:
Fixation of electronic components, housing elements. Sealing, sealing, fixing boxes and junction boxes during electrical work, filling gaps and voids.
Features:
tensile strength - 1.5 MPa
shear strength - 1.5 MPa
elongation at break - 200%
dielectric strength - 12 kV/mm
thermal conductivity - 1.2 W/m * K
resistivity - 2 * 10 15 Ohm
operating temperature range - -60°C+250°C
initial curing time at 25°C - 10 min.
Directions for use:
The surfaces must be clean and dry. You can use isopropyl alcohol and a tissue for cleaning.
Remove the cap of the tube and secure the nozzle, then apply an even layer. Full cure time of the adhesive sealant is 24 hours at room temperature.
Скорее всего должен подойти, т.к. при застывании не твердеет до состояния камня, а похож на резину и поэтому будет гасить колебания и не будет трескаться.
The data presented in the product description are for reference only and may differ from those indicated by the manufacturer.
To carry out technical calculations and obtain the exact parameters of the goods, use the datasheets from the manufacturer's website.
If you need additional information, or you found an error in the description, or have other questions about this product, then our manager will help you: Вячеслав
unknown
The data presented in the product description are for reference only and may differ from those indicated by the manufacturer.